Resumen
MARE, G.S. y GROOT, D.. Improving the quality of tinplated steel using a novel technique to study the effect of industrial process parameters. J. S. Afr. Inst. Min. Metall. [online]. 2010, vol.110, n.4, pp.177-186. ISSN 2411-9717.
Tin plating operations are of a complex nature due to the many operational variables that need to be controlled in order to create a product of required quality. The work in this report lays the basics for the control of a halogen plating operation based on the DuPont tinplating set-up with regard to the chemical make-up of the plating solution, as well as operational variables such as temperature and current density. To evaluate these aspects of the process, a rotating cathode Hull-cell set-up was used. This allowed for a laboratory scale plating arrangement that simulates industry closely with regard to chemical and hydro-dynamic considerations. Typical industry accepted standards were obtained for the values of operational variables and a 'baseline' test was conducted employing these standards. All subsequent tests conducted were benchmarked against this baseline result. A large suite of results was obtained in which it was found that changes could be made to the industry accepted norm which would improve on the stability of the operation and therefore the quality of the final tin-plated product. Examples of these results are: an increase in stannous tin concentration, an increase in sodium chloride concentration and a slightly elevated plating temperature. In addition, conditions were found that must be avoided to prevent instability and poor product quality