TECHNICAL PAPER
Mechanical properties, durability characteristics and shrinkage of plain cement and fly ash concretes subjected to accelerated carbonation curing
R A Assaggaf; S K Adekunle; S Ahmad; M Maslehuddin; O S B Al-Amoudi; S I Ali
ABSTRACT
The paper presents an experimental study on assessment of the effect of accelerated carbonation curing (ACC) on the performance of two concrete mixtures having the same mixture proportions but different cementitious materials (plain-cement and fly-ash-blended-cement). Different sets of specimens were cast utilising both concrete mixtures and were then subjected to ACC for ten hours at a constant pressure of 414 kPa (60 psi). After exposing the specimens to ACC, they were tested for weight gain, carbonation depth, compressive and tensile strengths, modulus of elasticity, water penetration depth, rapid chloride permeability, shrinkage, SEM and XRD. ACC of the concrete specimens for ten hours resulted in a significant weight gain with less than 2 mm of carbonation depth. Both mixtures gained compressive strength above 20 MPa after ten hours of ACC. The strength increased further when ACC-treated specimens were exposed to air, with a significant increase up to seven days for plain-cement concrete and up to 28 days for fly-ash-blended-cement concrete. Compared to reference moist-cured concretes, the ACC-treated concretes were found to exhibit a slightly lower long-term strength (15% for plain-cement and 5% for fly-ash-concrete). However, the overall performance of the ACC-treated concrete mixtures was comparable with the respective moist-cured concrete mixtures.
Keywords: accelerated carbonation curing, concrete, mechanical properties, durability, shrinkage
INTRODUCTION
Carbonation is a process in which the present in the atmosphere penetrates concrete and reacts with calcium hydroxide Ca(OH)2 to form calcium carbonates CaCO3 (Rostami et al 2012). This chemical reaction is considered harmful to concrete durability characteristics if it is allowed to occur for a long period, since it is associated with a significant decrease in the pH of concrete, which in turn leads to the initiation of corrosion of steel bars embedded in the concrete when the concrete pH falls below a threshold value of about 10.
However, accelerated carbonation curing (ACC), which involves exposing concrete to CO2 under pressure for a short duration of time at an early age (after a few hours of casting), has been reported to improve the mechanical and durability properties of hardened concrete (Rostami et al 2012). The CO2 sequestered into young concrete reacts with Ca(OH)2 and C-S-H generated by the cement hydra tion process, leading to the formation of geologically stable calcium carbonates (Rostami et al 2012; Fernandez Bertos et al 2004; Mo & Panesar 2013; Shao et al 2014). Unlike the long-term natural carbonation process of hardened concrete, which has been the focus of several research studies on concrete durability, ACC eliminates the loss-of-alkalinity problem, since the accompanying reduction in pH occurs to a negligible depth below the concrete surface, rather than in the concrete core. Therefore, reinforcing steel bars are safe from de-alkalisation-induced reinforcement corrosion (Rostami et al 2012; Shao et al 2014; Monkman & Shao 2010).
ACC changes the mineralogy, morphology and microstructure of concrete, leading to an increase in the density of concrete, which implies higher strength and durability, compared to that offered by the microstructure of concrete developed by conventional curing (Rostami et al 2012; Mo & Panesar 2013; Pizzol et al 2014). In addition, ACC involving sequestration of CO2 in concrete helps in reducing the carbon footprint, mitigating the environmental problems associated with cement and concrete production.
Many factors affect the effectiveness of ACC, such as the concentration of CO2, temperature, relative humidity, pressure in the carbonation chamber, exposure duration to CO2, the age of concrete when exposed to CO2, type and amount of binders, and water/cement ratio (Fernandez Bertos et al 2004; Chen et al 2011; El-hassan et al 2013; Mohammed et al 2014; Shao & Monkman 2006; Zhan et al 2013a; Zhan et al 2013b). Kashef-Haghighi and Ghoshal (2013) found that CO2 uptake could be increased significantly through the use of cements having higher amounts of reactive minerals and more fineness, which would provide a higher reactive surface area. Carbonation shrinkage resulting from ACC can be reduced by incorporating mineral admixtures such as slag (Monkman & Shao 2010). Rostami et al (2012) reported that keeping specimens in the air for some time before exposure to CO2 is very important to allow better diffusion of CO2 into concrete.
The consumption of CO2, captured from the manmade stationary sources of CO2 emissions and stored for usage (carbon capture), in ACC of concrete would significantly help in reducing the global greenhouse gas emission and, therefore, the problems around global warming, which are of great environmental concern. About 1.5 million tons of CO2 can be sequestered in concrete products made with 16.4 million tons of cement in the USA, based on about 9% of CO2 by mass of cement (Kashef-Haghighi & Ghoshal 2013).
The present study was conducted to investigate the mechanical properties, durability characteristics, shrinkage and microstructure of plain-cement and fly-ash-blended-concrete mixtures cured using accelerated carbonation. The main objective of the present work was to explore the possibility of using ACC as an alternative curing method that can be adopted by precast concrete industries.
EXPERIMENTAL PROGRAMME
Materials
ASTM C 150 Type I Portland cement with a specific gravity of 3.15 was used in this study to prepare the concrete specimens. A class F fly ash was used to prepare the concrete mixture, consisting of a blend of Portland cement and fly ash. Table 1 shows the chemical compositions of Portland cement and fly ash used in this work.
Coarse aggregate with a maximum size of 12 mm, specific gravity of 2.60 and water absorption of 1.4% was used. Dune sand with a specific gravity of 2.56 and water absorption of 0.4% was used as fine aggregate. Figure 1 shows the grading curves of coarse and fine aggregates. CO2 gas with 99.9% purity was used for carrying out ACC of the concrete specimens.
Concrete mixtures
Two concrete mixtures having the same mixture proportions, but with different cementitious materials, were considered in this study. The first mixture was prepared with a plain Portland cement as a cementi-tious material, and this concrete mixture was abbreviated as plain-cement concrete (PCC). In the second mixture, a blend of 20% fly ash and 80% Portland cement was used as cementitious material and this concrete mixture was abbreviated as fly-ash-blended-cement-concrete (FA-BCC). Table 2 shows the weights of the constituent materials for preparing one cubic metre of each of these two concrete mixtures, PCC and FA-BCC. Both concrete mixtures were prepared with a water-to-cementi-tious material ratio of 0.45 to maintain a slump of 100 mm (±20 mm).
Setup for Acc
The setup used for ACC of the concrete mixtures was the same as that used for a previous experimental study reported elsewhere (Ahmad et al 2017). The inner diameter and height of the purpose-built ACC cylindrical chamber were 400 and 500 mm, respectively. Three holes were made through the wall of the chamber. The inlet hole was connected to the CO2 cylinder, while the second hole was connected to a pressure gauge to measure the pressure in the ACC chamber. The outlet hole was made to flush out the CO2 from the chamber after curing. To ensure operational safety, the chamber was made of steel with a wall thickness of 8 mm.
Preparation and curing of concrete specimens
The specimens made of both concrete mixtures were demolded after 18 hours of casting, and the specimens of each of the two concrete mixtures were divided into two sets. One set of specimens was cured by ACC for ten hours, while the other set was moist-cured for seven days. ACC was carried out by exposing the specimens to CO2 in the ACC chamber where a constant pressure of 414 kPa (60 psi) was maintained for a period of ten hours, in accordance with the optimum levels of pressure and CO2 exposure duration, as reported in a preliminary study (Ahmad et al 2017). The moist-curing was carried out by sandwiching the specimens in layers of burlap in a curing chamber, which was kept continuously moist for a period of seven days. The initial compressive strength of each concrete mixture was determined by crushing four cubes of 50 mm size immediately after demolding.
Prior to applying ACC, all specimens were weighed using a precision electronic balance with a resolution of 0.01 g. Thereafter, the specimens were arranged inside the ACC chamber on a perforated platform. The flow control valve of the CO2 gas cylinder was then released while the chamber outlet was still open. This step was continued for one minute to clean the chamber before ACC commenced. Subsequently, the outlet was closed, and the pressure regulator was adjusted to maintain a constant ACC pressure of 414 kPa (60 psi). The ACC process continued for ten hours before the cured specimens were taken out of the chamber. The post-ACC weight gain was recorded.
After the curing process for both ACC and moist-curing regimes, the specimens were tested to assess their mechanical properties, durability characteristics, shrinkage behaviour and microstructure.
Microstructure and identification of carbonation products
The morphology of the carbonated hydration products was studied by examining the secondary electron image (SEI) of near-surface zones of fractured concrete samples under a JEOL (JSM-6610LV model) scanning electron microscope (SEM), which was equipped with an energy dispersive spectroscopy (EDS) detector. Additionally, crystalline phases present in the ACC-cured specimens were analysed by X-ray diffraction (XRD), using a Rigaku (Ultima IV model) X-ray diffractometer with Cu-Ka radiation (X = 1.5418 A), over a 26 range of 10 to 70° in steps of 0.02° 26.
The near-surface samples used for the microstructure studies in this work were carefully collected to ensure the exclusion of coarse aggregates in order to isolate only the mortar phase of the concrete mixtures.
RESULTS AND DISCUSSION
Weight gain observations
For each of the two concrete mixtures, the weight gain was calculated after exposing 20 cube specimens to ACC for ten hours at 414 kPa. The specimens were weighed before and after ACC to determine the average CO2 uptake of each mixture, expressed as percentage weight gain by mass of cement. Figure 2 shows the weight gain for the two concrete mixtures considered in this study. It can be seen from Figure 2 that FA-BCC had a 13% lower weight gain, compared to PCC. This can be attributed to the availability of a lower amount of hydration-generated Ca(OH)2 for CO2 uptake in FA-BCC, where 20% of Portland cement was replaced by fly ash.
Carbonation depth
After exposure to ACC, the carbonation depths were measured by splitting the specimens into two and then spraying phenolphthalein solution on the split surfaces of concrete. The carbonation depth was indicated by the thin outer layer of the discoloured portion of the concrete surface. Figure 3 schematically shows the carbona-tion profile, indicated by the portion with phenolphthalein staining (represented by the black colouring) and the colourless portion (represented by white colouring) on the fractured surface of a concrete specimen after exposed to ACC. For each sample, the carbonation depth was taken as the average value of the largest CO2 penetration depth measured on all sides of the sample, as indicated in Figure 3.
Table 3 presents the average carbonation depths in mm for the two concrete mixtures considered in this study. It can be observed from Table 3 that the carbonation depth was around 2 mm for both concrete mixtures studied. However, FA-BCC experienced a slightly (11%) higher carbonation depth than PCC. A reverse of this observation might be expected, because a higher CO2 uptake was recorded for the plain cement mixture. However, it is known that the pozzolanic action of fly ash is a slow process. Therefore, after 18 hours of casting when ACC commenced, the lower cement content in the FA-BCC would result in higher gas porosity because of the lower density of the primary C-S-H gel in the mixture. In addition, for the same reason (lower cement content), the lower amount of Ca(OH)2 available for CO2 uptake also poses less hindrance to further penetration at later stages of carbonation. Hence, the higher penetration depth in the fly ash mixture, despite its lower CO2 uptake, can be justified. Subsequently, the lower reduction of CO2 uptake of the fly ash mixture (13%), compared to the 20% reduction of cement content, can be explained by the deeper reach of the CO2 front.
It is worth noting that the carbonation depth obtained using the method described earlier is an underestimate of the true depth of the carbonation front. Phenolphthalein indication only highlights the region with pH lower than 10. This implies that the measured average depth does not include the carbonated regions that are deeper than the phenolphthalein-highlighted zone of which the pH levels are higher than the sensitive range of phenolphthalein indicator. Nevertheless, the actual depth of carbon-ation is not expected to exceed two to three times that obtained through phenolphtha-lein indication measurements, which does not constitute a threat of corrosion to a steel bar embedded in a reinforced concrete element made with these mixtures, since the usual minimum cover to rebars is 20 mm. In addition, ACC of concrete elements results in densification of the thin carbonated surface layer (or skincrete). The densification of skincrete is expected to slow down the diffusion rate of CO2 into concrete through the skincrete, leading to higher resistance to natural carbonation during the service life of the concrete element. Further, subsequent hydration of CO2-cured concrete (upon contact with water) re-alkanises the concrete to pH in excess of 12.0 (Zhang & Shao 2016), offering additional protection of CO2-cured concrete from natural carbonation during the service life.
Evolution of compressive strength
For concrete specimens subjected to ACC regime, the first test was conducted directly after ten hours of ACC, while the first test on specimens exposed to moist-curing regime was carried out after seven days of moist-curing. Subsequently, concrete specimens from both curing regimes were subjected to air-curing under laboratory conditions and were tested after 7, 14, 28 and 90 days of additional air-curing. The compressive strength development of PCC and fly ash FA-BCC for both ACC and moist-curing are shown in Figures 4 and 5.
It can be observed from Figures 4 and 5 that both PCC and FA-BCC gained a compressive strength of more than 20 MPa only after subjecting them to ten hours of the ACC.
As can be seen from Figure 4, the ACC specimens achieved a higher compressive strength during the first seven days of air exposure. About 63% increase in the com-pressive strength due to the air-curing for the first seven days after ACC was recorded. However, very little benefit of post-ACC air-curing was observed after the first seven days of air exposure, as is evident from the nearly flat portion of strength evolution curve shown in Figure 4. A similar trend of strength evolution was observed for moist-cured specimens. An increase of about 30% in compressive strength was noted when moist-cured specimens were exposed to air for the first seven days. As in the case of ACC, the benefit of air exposure after moist-curing was found to be insignificant beyond seven days of air exposure.
It is important to note from Figure 4 that the strength of ACC specimens after seven days in the air was found to be about 14% higher than the strength of seven days moist-cured specimens. However, the strength of moist-cured specimens kept in the air for seven days was found to be around 10% higher than the strength of ACC specimens kept in the air for 14 days. This can be explained by the fact that the carbonation process is of exothermic nature. The heat generated from the process tends to increase the cement hydration rate as ACC progresses. Additionally, during the post-ACC air exposure, the carbonated layer around the surface of the ACC specimen significantly reduced the evaporation of moisture from the core of the specimens, which resulted in continuation of the hydration process until most of the free concrete water had been consumed, resulting in a lower rate of strength gain. On the contrary, in the specimens subjected to seven days moist-curing, the rate of strength gain during the moist-curing period was slower than that of ACC specimens exposed to the air for seven days, due to the absence of carbonation-induced heating. Due to the slow rate of hydration, the amount of residual moisture available in the pores of moist-cured specimens would be more than that of ACC specimens (because ACC specimens consumed almost entire pore water for further hydration during the first seven days of air exposure). This therefore explains the observed higher strength gain during air exposure of moist-cured specimens compared to ACC specimens.
It can further be seen that the difference in the strength of ACC and moist-cured specimens is almost constant (about 15%) during the long-term air exposure. Therefore, it may be concluded that the difference in the strength of ACC and moist-cured specimens can be taken as 15% during the service life of the concrete. It is worth mentioning that the ACC concrete achieved a strength of 27 MPa only after ten hours of accelerated carbonation, making it possible to handle the carbonation-cured concrete only after ten hours of curing.
Figure 5 shows the plot of compressive strength evolution of FA-BCC, in which 20% of cement was replaced by fly ash. It can be seen from Figure 5 that the ACC specimens exposed to air for the first seven days achieved 59% higher strength than that recorded immediately after the ACC. The increase in the strength of moist-cured specimens after the first seven days of air exposure was only about 10%.
However, unlike the PCC made with only cement as binder, the strength of ACC specimens made of FA-BCC after exposure to air for seven days is almost similar to that of the seven days moist-cured specimens of FA-BCC. This observation may be explained by the relatively lower degree of carbonation achieved for FA-BCC due to the availability of a lower amount of Ca(OH)2, as a result of its lower cement content. This relatively lower amount of Ca(OH)2 was further reduced in secondary hydration with silica from the admixed fly ash. Due to the lower degree of carbonation, the enhancement of strength owing to the increased surface hardness was relatively lower, leading to the development of lower strength.
Unlike the case of PCC, where the rate of strength gain became almost negligible after seven days of air exposure of both ACC as well as moist-cured specimens, the rate of strength gain for both curing regimes in the case of FA-BCC was considerable up to 28 days of air exposure, as can be seen from Figure 5. This can be attributed to the slow rate of hydration due to the addition of fly ash to FA-BCC, which involved secondary hydration.
Furthermore, it can be seen from Figure 5 that the difference in the strength of ACC and moist-cured specimens is almost constant (by around 5%) during the long-term air exposure. Therefore, it may be concluded that the difference in the strength of ACC and moist-cured specimens of FA-BCC will be taken as only 5% during the service life of concrete. Again, it must be note that the FA-BCC subjected to ACC achieved a strength of 24 MPa only after ten hours of carbonation.
Splitting tensile strength
Figure 6 shows the values of splitting tensile strength of both concrete mixtures at an age of 14 days for both ACC and moist-curing regimes. As can be seen from Figure 6, ACC appears to improve the tensile strength for PCC by 21% in comparison with the moist-curing regime, while a reversed situation is noted in the case of FA-BCC. However, even in the case of FA-BCC, the ACC regime maintained a tensile strength falling within the range recommended for a structural concrete mixture.
Elastic modulus
Figure 7 illustrates the 14-day chord modulus values for the two concrete mixtures subjected to ACC and moist-curing. Specimens subjected to ACC exhibited a slightly lower stiffness than that of the moist-cured specimens for both mixtures. However, for both mixtures, the reduction was less than 10% with respect to moist-cured specimens. This slight stiffness reduction is still in line with the little reduction in strength of ACC specimens at 14 days, in relation to moist-cured specimens. Therefore, it can be concluded that the elastic modulus of ACC specimens is comparable to that of the moist-cured specimens.
Water and chloride permeability
Figure 8 presents the water penetration depths, performed according to the DIN 1048 standard (DIN 2004), for the two concrete mixtures, PCC and FA-BCC. In each mixture, the test was conducted for both ACC and moist-cured specimens at 14 days of concrete age. It can be observed from Figure 8 that the specimens made of PCC and subjected to ACC had a slightly lower water penetration depth than that of the moist-cured specimens. By making a connection to the higher CO2 uptake in PCC and lower CO2 penetration depth (as discussed earlier), ACC specimens are expected to exhibit higher surface layer density. This is in agreement with the claim that the carbonation of concrete makes the microstructure of concrete surface denser, thereby decreasing the porosity of the surface layer of concrete that resists fluid penetration (Ahmad et al 2017). Although the improvement of the surface density is not significant, as indicated by water penetration depth, it can be inferred that ACC does not have negative effects on the properties of PCC.
On the other hand, a higher water penetration depth was noted in specimens made of FA-BCC and subjected to ACC compared to moist-cured specimens. A converse of the case for PCC may be used to explain this observation. FA-BCC exhibited lower CO2 uptake than PCC, as a result of a lower amount of Ca(OH)2 at the time of ACC, and for the same reason it also exhibited a higher CO2 penetration depth. The combined effects of these two factors tend to reduce the surface layer density of FA-BCC ACC specimens, hence the recorded larger water penetration depth.
Figure 9 presents the results of the rapid chloride permeability test, performed according to the ASTM C1202 standard (ASTM 2012), for the two concrete mixtures. Even though the results are in the same range of 'moderate permeability' according to the referenced standard's classification, the behaviour pattern recorded here is similar to that of the water permeability test.
Drying shrinkage
Figures 10 and 11 show the variations of drying shrinkage strain with time for ACC and moist-cured specimens belonging to PCC and FA-BCC mixtures, respectively. For the two concrete mixtures, the recorded drying shrinkage in ACC specimens was higher than that in moist-cured specimens, as is evident from Figures 10 and 11. Higher shrinkage in ACC specimens may be attributed to the shrinkage action associated with the chemical reactions involved in carbona-tion of the surface concrete, as well as the accompanying moisture loss to the exothermic process. It should be stated that the ACC-induced shrinkage can be controlled by spraying water on carbonated concrete immediately after ACC to compensate for the water loss during the ACC process which may significantly reduce the shrinkage.
Concrete microstructure characterisation
Figure 12 shows a micrograph of a fractured specimen exposed to ACC. The lower edge of the image is the edge of the concrete sample exposed to ACC. The red line indicates the actual profile of the carbonated area penetrated by CO2. The dense structure of hydrates shown in Figure 12 is attributed to the formation of CaCO3 which was caused by the accelerated carbonation of Ca(OH)2 (portlandite) and conventional calcium silicate hydrate (C-S-H). The intermixing between CaCO3 and C-S-H may be explained by the fact that the primary C-S-H was highly porous after about 18 hours of casting when the ACC was commenced. Therefore, the pores were available for diffusion of CO2 and its associated reaction with the portlandite formed during the primary hydration process, resulting in the formation of CaCO3. Based on the scale of the SEM image, the carbonation depth was estimated as 80 |im at the section imaged. Obviously, ACC reduced the permeability significantly by filling the pores and minor cracks with CaCO3. Furthermore, this layer may reduce the evaporation of the internal water in the long term, imparting a self-curing ability to the concrete. All these explain the improved properties of the concrete cured with the ACC method.
In addition to the SEM imaging, the chemistry of selected areas of carbonated regions of near-surface concrete samples was also examined through quantitative EDS analysis (QEDS). Figure 13(a) shows the EDS profile of the area marked 'spectrum 8' in Figure 12 for a PCC sample exposed to ACC.
The EDS shown in Figure 13(a) indicates a high carbon content of 18.9% and a low amount of silica at 3.1 %. Since the mortar phase sample examined was free of limestone aggregates (as seen in Figure 12), the high carbon content captured by the QEDS implies that the examined region of the carbonated specimen contained a significant amount of carbonation products. Figure 14(a) depicts the mineralogical composition of concrete specimens cured with the ACC method. The presence of calcite of about 25% by mass of the tested sample was noted. This observation implies that most of the high amount of carbon indicated by QEDS was from calcite that resulted from the reaction of CO2 with portlandite, as well as carbonated C-S-H gels.
A micrograph of a fractured sample of FA-BCC concrete specimen exposed to ACC is shown in Figure 15. Some carbonation products can be recognised, but the amount of CaCO3 produced was less than that of PCC. This reinforces previous analyses establishing a lower degree of carbonation as a result of lower cement content in FA-BCC. Figure 13(b) shows the EDS of the area shown in Figure 15 ('Spectrum 4'). The EDS established the fact that ACC of FA-BCC resulted in a lower degree of carbonation than that in PCC, since the amount of silica detected was slightly higher (8.7%) compared to the case of the PCC sample (3.1°%). Furthermore, XRD of the PCC sample indicated a calcite content of 24.6% (Figure 14(a)), while the FA-BCC sample contained only 15.2% (Figure 14(b)).
Therefore, it can be concluded that the negative effect of ACC on the measured durability indices (water permeability and chloride permeability) of the FA-BCC, as a combined result of a lower degree of car-bonation and deeper penetration of CO2, has been well captured by morphological and chemical analyses.
CONCLUSIONS
From the results presented and the explanations offered for the reported observations, the following conclusions can be drawn:
■ The carbonation depth was in the order of a few mm for both concrete mixtures, which may be considered a safe depth for a reinforced concrete element against reinforcement corrosion.
■ Carbonation depth and weight gain analyses have established that the higher strength gain in plain-cement mixture can be attributed to a higher degree of carbonation coupled with lower depth of CO2 penetration.
■ An increase in the compressive strength by around 60% was recorded in both mixtures when they were exposed to air-curing for seven days after ten hours of ACC.
■ ACC specimens exhibited 5 to 15% lower long-term strength compared to moist-cured specimens, indicating that the ultimate strength of concrete exposed to ACC is not much different from that of the concrete exposed to seven days of moist-curing.
■ Although the shrinkage of ACC-treated specimens was generally higher than that of moist-cured specimens for the two concrete mixtures studied, post-ACC water spraying was required to compensate for the water loss during the ACC process.
■ The tensile strength and modulus of elasticity of the ACC specimens were found to be comparable to those of moist-cured specimens. However, the measured durability indices indicated some negative effect of ACC on the durability characteristics of fly-ash-concrete, while the plain-cement-concrete exhibited improved durability characteristics.
■ The negative effect of ACC on the measured durability indices of the fly-ash-concrete was well captured by morphological and chemical analyses, through SEM and XRD.
ACKNOWLEDGEMENTS
The authors gratefully acknowledge the financial support provided by King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia, under research grant Projects No RG1323-1 and RG1323-2. The logistical support of the Department of Civil and Environmental Engineering, and the Research Institute at the same university is also acknowledged with appreciation.
REFERENCES
Ahmad, S, Assaggaf, R A, Maslehuddin, M, Al-amoudi, O S B, Adekunle, S K & Ali, S I 2017. Effects of carbonation pressure and duration on strength evolution of concrete subjected to accelerated carbonation curing. Construction and Building Materials, 136: 565-573. [ Links ]
ASTM (American Society for Testing and Materials) 2012. Standard Test Method for Electrical Indication of Concrete's Ability to Resist Chloride Ion Penetration. Philadelphia, PA: ASTM. [ Links ]
Chen, D-P, Liu, J & Liu, M 2011. Accelerated carbonation curing of foam concrete with lower density. Presented at the 1st International Conference on Civil Engineering, Architecture and Building Materials (CEABM 2011), Haikou, China. Published in Advanced Materials Research, 250-253: 172-177. [ Links ]
DIN (Deutsches Institut für Normung) 2004. DIN 1048. Test Methods of Concrete Impermeability to Water: Part 2. Berlin: DIN. [ Links ]
El-hassan, H, Shao, Y & Ghouleh, Z 2013. Reaction products in carbonation-cured lightweight concrete. ASCE Journal of Materials in Civil Engineering, 25 (June): 799-809. [ Links ]
Fernández Bertos, M, Simons, S J R, Hills, C D & Carey, P J 2004. A review of accelerated carbonation technology in the treatment of cement-based materials and sequestration of CCO2. Journal of Hazardous Materials, 112(3): 193-205. [ Links ]
Kashef-Haghighi, S & Ghoshal, S 2013. Physico-chemical processes limiting CO2 uptake in concrete during accelerated carbonation curing. Industrial and Engineering Chemistry Research, 52(16): 5529-5537. [ Links ]
Mo, L & Panesar, D K 2013. Accelerated carbonation - A potential approach to sequester CO2 in cement paste containing slag and reactive MgC. Cement and Concrete Composites, 43: 69-77. [ Links ]
Mohammed, M K, Dawson, A R & Thom, N H 2014. Carbonation of filler typed self-compacting concrete and its impact on the microstructure by utilization of 100% CO2 accelerating techniques. Construction and Building Materials, 50: 508-516. [ Links ]
Monkman, S & Shao, Y 2010. Integration of carbon sequestration into curing process of precast concrete. Canadian Journal of Civil Engineering, 37(2): 302-310. [ Links ]
Pizzol, V D, Mendes, L M, Savastano, H, Frías, M, Davila, F J, Cincotto, M A et al 2014. Mineralogical and microstructural changes promoted by accelerated carbonation and ageing cycles of hybrid fiber-cement composites. Construction and Building Materials, 68: 750-756. [ Links ]
Rostami, V, Shao, Y, Boyd, A J & He, Z 2012. Microstructure of cement paste subject to early carbonation curing. Cement and Concrete Research, 42(1): 186-193. [ Links ]
Shao, Y & Monkman, S 2006. A new CO2 sequestration process via concrete products production. Proceedings, 2006 IEEE EIC Climate Change Conference, Cttawa, Canada. [ Links ]
Shao, Y, Rostami, V, He, Z & Boyd, A J 2014. Accelerated carbonation of Portland limestone cement. Journal of Materials in Civil Engineering, 26(1): 117-124. [ Links ]
Zhan, B, Poon, C & Shi, C 2013. CO2 curing for improving the properties of concrete blocks containing recycled aggregates. Cement and Concrete Composites, 42: 1-8. [ Links ]
Zhan, B, Poon, C S, Liu, Q, Kou, S & Shi, C 2013. Experimental study on CO2curing for enhancement of recycled aggregate properties. Construction and Building Materials, 67: 3-7. [ Links ]
Zhang, D & Shao, Y 2016. Early age carbonation curing for precast reinforced concretes. Construction and Building Materials, 113: 134-143. [ Links ]
Correspondence:
RIDA ALWI ASSAGGAF
Civil and Environmental Engineering Department
King Fahd University of Petroleum and Minerals
Dhahran 31261, Saudi Arabia
T: +966 5386 55266
E: g201206100@kfupm.edu.sa
PROF SAHEED KOLAWOLE ADEKUNLE
Civil and Environmental Engineering Department
King Fahd University of Petroleum and Minerals
Dhahran 31261, Saudi Arabia
T: +966 5326 55414, E: saheedka@kfupm.edu.sa
PROF SHAMSAD AHMAD
Civil and Environmental Engineering Department
King Fahd University of Petroleum and Minerals
Dhahran 31261, Saudi Arabia
T: +966 13 860 2572, E: shamsad@kfupm.edu.sa
DR MOHAMMED MASLEHUDDIN
Research Institute
King Fahd University of Petroleum and Minerals
Dhahran 31261, Saudi Arabia
T: +966 5000 26404, E: muddin@kfupm.edu.sa
SYED IMRAN ALI
Research Engineer
Civil and Environmental Engineering Department
King Fahd University of Petroleum and Minerals
Dhahran 31261, Saudi Arabia
T: +966 5070 02306, E: saimran@kfupm.edu.sa
PROF OMAR S BAGHABRA AL-AMOUDI
Civil and Environmental Engineering Department
King Fahd University of Petroleum and Minerals
Dhahran 31261, Saudi Arabia
T: +966 5057 58489, E: amoudi@kfupm.edu.sa
RIDA ALWI ASSAGGAF is presently a PhD student in the Civil and Environmental Engineering Department at King Fahd University of Petroleum and Minerals, Saudi Arabia. He did his MS dissertation work on accelerated carbo nation curing of concrete.
PROF SAHEED KOLAWOLE ADEKUNLE holds a PhD (Civil Engineering) from King Fahd University of Petroleum and Minerals, Saudi Arabia. Presently he is working as Assistant Professor in the Civil and Environmental Engineering Department at the same university. He has research expertise in the field of structural engineering, computational engineering, concrete science and engineering, finite element methods, meshless and hybrid numerical methods, software development for engineering analyses, and corrosion of steel reinforcement. He has published several research papers in ISI journals and has refereed conference proceedings.
PROF SHAMSAD AHMAD holds a PhD (Civil Engineering) from the Indian Institute of Technology (IIT), Delhi, India. Presently he is a Professor in the Civil and Environmental Engineering Department at King Fahd University of Petroleum and Minerals (KFUPM), Saudi Arabia. He has been involved in several funded research projects. His research interests include corrosion of steel in concrete structures, characterisation of structural materials, utilisation of industrial solid wastes as structural materials, cement-based solidification/stabilisation of wastes and contaminated soil, sludge, etc, and applications of optimisation techniques. He has published over 80 research papers in refereed journals and conference proceedings. He received KFUPM Excellence in Research Awards in 2010/11 and 2015/16.
DR MOHAMMED MASLEHUDDIN obtained his PhD (Civil Engineering) from Aston University, Birmingham, England. He is currently a Senior Research Engineer (equivalent to full Professor) in the Research Institute, King Fahd University of Petroleum and Minerals, Saudi Arabia. He has vast research experience, has published more than 180 technical papers in refereed journals, and has reviewed conference proceedings in the fields of structural materials and durability of concrete.
SYED IMRAN ALI holds an MS in Structures and Materials from King Fahd University of Petroleum and Minerals, Saudi Arabia. He is a Research Engineer in the Civil and Environmental Engineering Department of the same university. For the lasts 14 years he has been deeply involved in experimental work and data analysis for several projects related to the work presented in this paper.
PROF OMAR S BAGHABRA AL-AMOUDI holds a PhD (Civil Engineering) from King Fahd University of Petroleum and Minerals (KFUPM), Saudi Arabia. Presently, he is working as Professor in the Civil and Environmental Engineering Department, KFUPM. He has extensive research experience in concrete durability and Sabkha-materials interaction and stabilisation of indigenous soils. He has published more than 150 papers in refereed journals and conference proceedings. He is a recipient of several research awards from KFUPM and other organisations in Saudi Arabia, and enjoys international recognitions for his contribution to concrete research.